Details

---

Description :

Features :

• Repairs leak in 30 minutes
• Applicable to pipes up to 18' (457 mm) diameter
• Applicable on any metal or non-metal pipes
• Repairs T-joint, elbow joint, valve thread, valve body
• Withstand pressure up to 400 psi (28 kg/cm²)
• Withstand temperature up to 200 °C (392 °F)
• Safe for drinking water and resistant to most chemicals
• Reinforce and strengthen pipe after repair
• Permanent repair and extend service life of pipes

Applicable Materials :

• Steel
• Copper
• Aluminium
• Galvanized steel
• PVC
• CPVC
• Stainless steel
• Polyethylene
• Polypropylene
• Cast-iron
• Concrete
• FRP/GRE

Chemical Resistance

• Oil
• Water (drinking water, wastewater, steam)
• Solvents (acetone, toluene, MEK, ethyl alcohol)
• Mild acids (hydrochloric acid, sulfuric acid) and alkalis
• Chemical (ethylene glycol, xylenes, ammonia)
• Hydrocarbons
• Bases
• Slurries
• Fuels (petroleum, diesels, gasoline)
• Gases (LNG, LPG)
• Organic salts

 
WORKING TIME (FIBERGLASS TAPE):

• 1 minute at 30 °C (86 °F)

CURING TIME:

• 30 minutes at 30 °C (86 °F)
• Heat may be applied to decrease curing time
• Unopened foil pouch may be immerse in cold water prior to repair to add working and curing time.

APPLICATION:

• Pipe repairs
• offline repairs
• sealing joints
• hazardous material spill control
• reinforce thinning walls
• Abrasion protection
• Structural reinforcement
• Repairs in hard to reach areas
• Underwater repairs

OPERATING TEMPERATURE:

• Continuous – From -29 °C (-20 °F) up to 200 °C (392 °F)
• Intermittent – From 200 °C (392 °F) up to 320 °C (570 °F)

OPERATING PRESSURE:

• Recommended for pressure up to 400 psi (28 kg/cm²)
• (Results vary depending on pipe size, type of pipe, hole size, pipe content and method of application)

TECHNICAL DATA:

Pressure tested	:	1/2' (15 mm) steel pipe with 1/8' (3 mm) hole when repaired with Wrap Seal withstands 4000 psi (281 kg/cm2)
		1/2' (15 mm) steel pipe with 1/2' (13 mm) hole when repaired with Wrap Seal withstands 600 psi (42 kg/cm2)
Tensile strength	:	3920 psi (276 kg/cm2)
Bond strength	:	230 psi (16 kg/cm2)
Tensile elongation	:	1.2 % ± 0.7 %
Compression strength	:	13750 ± 530 psi (967 ± 37 kg/cm2)
Yield strength	:	2260 psi (159 kg/cm2)
Cured hardness	:	82 Shore D